FIXTOP A and B Tenax Epoxy Mastic

FIXTOP A and B Tenax Epoxy Mastic Kg.2 

FIXTOP A and B Tenax Vertical two-component epoxy mastic in a beige thixotropic paste. Epoxy resin for bonding marble, stone, granite, quartz and ceramics. Fixtop is a resin with excellent bonding strength, good adhesion speed even with low thickness. Fixtop epoxy resin can also be used in mixed bonding such as: metal-stone, ceramic-stone, concrete-stone, concrete-metal, stone-composite panels such as honeycomb. The metal should be sanded before gluing. In this type of bonding it is suggested to check the flatness of the finished piece after one month.

Application:

• The resin and hardener must be stored in original cans.
• In automatic dosing systems, contact with metal parts of copper, brass and similar alloys that may rust is to be avoided.
• Use plastic resistant to corrosive liquids, never use PVC.
• Take from the two cans the necessary quantities, IN WEIGHT OR VOLUME, of the two components A and B, in the ratio 1: 1.
• Mix vigorously and proceed with use.
• Use clean tools during mixing. If necessary add colors and pigments.
• Make sure that the material on which the glue will be applied is completely dry and clean.
• For cleaning the equipment, use non-greasy solvents such as acetone and butyl acetate.

Technical Data:

• Viscosity part A cps 25 ° C Thixotropic paste
• Viscosity part B cps 25 ° C Thixotropic paste
• Density part A / part B at 25 ° C gr / cm³ 1.4 / 1.4
• Appearance part A Gray paste
• Appearance part B Beige pasta
• Appearance of hard gray resin
• Resin color in GARDNER ASTM D1544 NA
• Hardener color in GARDNER ASTM D1544 NA
• Mixing ratio by weight 100 + 100 = tot 200
• Mass gel time 25 ° C About 30-40 min
• Time out of touch at 25 ° C with 50% relative humidity about 2h30
• Time out of touch at 40 ° C with 10% relative humidity About 2h
• ShoreD hardness (1) ASTM D 2240 72
• Glass transition temperature Tglass (ASTM E1545) (1) n.d.
• Breakout force with glass mesh on marble (1) (ASTM D3167) 1.0 N / mm
• Marble adhesion strength (ASTM D4541) (1) 14 Mpa
• Adhesion force on glass (ASTM D4541) (1) 14 Mpa T
• Est aging in climatic cell Qsun (ASTM D904) 3 years outdoor (light + rain + heat shock) passes the test, no detachment of the resin from the support Yellowing at Xenon solar test 3 years (ISO11341) high
• Minimum reaction temperature + 10 ° C T
• Minimum emperature use after hardening -25 ° C
• Maximum temperature of use after hardening + 60 ° C
• Workability time at 25 ° C (minimum time for polishing and cutting) 24 hours